Article No. 094401
Rigid two-component EP resin for frictional injection into concrete building elements, F-I (P)/F-V (P)
Product specifications
* after 7 days at 23 °C
The stated values represent typical product characteristics and are not to be construed as binding product specifications.
Field of application
- Crack injection in concrete according to DIN EN 1504-5
- Classification: U(F1) W(1) (1/2) (8/30)
- Moisture level: DY, DP
- Frictional bonding and joining of components
- Strengthening open-pored concrete structures
- Joining hollow components
Properties
- Freeze/thaw resistant
- High chemical resistance
- Total solid (Similar to the testing method of Deutsche Bauchemie e.V.)
- Fire behaviour B2 pursuant to DIN 4102-4
- Low viscosity
-
Preparation
-
Substrate requirements
The flanks of the crack must be dimensionally stable and free from loose parts, sintered layers, oils, grease and other separating substances.
-
Preparations
Plug the path of the crack if necessary.
-
-
Preparation
-
Combination container
Add the entire quantity of the hardener (component B) to the base compound (component A).
Mix thoroughly with a slow-speed electric mixer
(approx. 300 - 400 rpm).Mix for at least 3 minutes.
Insufficient mixing is indicated by streaks forming.
Pour the mixture into a separate container and mix again thoroughly.
-
Application
-
Application requirements
Temperature of the material, air and substrate: min. 8 °C
-
Application instructions
-
As a general principle, higher temperatures will reduce and lower temperatures will increase the times stated.
Significant increase in viscosity at low temperatures.
-
-
Working tools / cleaning
-
Suitable mixer
-
More detailed information can be found in the Remmers Tool Programme.
Clean tools, equipment and splashed material immediately while fresh with V 101.
Take suitable protective and waste disposal measures when cleaning.
-
-
Storage / shelf life
-
If stored unopened in the original container and kept cool, dry and protected from frost, min. 12 months (component A)/min. 24 months (component B).
-
Usage
-
- To be determined on a case-by-case basis, depending on the crack width and component thickness
- Approx. 1.1 kg/l void
- Approx. 0.4-0.7 kg/running metre
-
General information
-
Unless otherwise specified, all of the values and application rates given above have been determined under laboratory conditions (20 °C). Slight deviations from these values may arise if the product is worked with on site.
The actual amount of material needed depends on the size of the void. Proceed based on the results of the building condition analysis.
Remember that surplus material may be needed depending on the application method.The current technical regulations must be observed.
-
-
Disposal instructions
-
Larger quantities of leftover product should be disposed of in the original containers in accordance with the applicable regulations. Completely empty, clean containers should be recycled. Do not dispose of together with household waste. Do not allow to enter the sewage system. Do not empty into drains.
-
-
Safety / regulations
-
Further information concerning safety during transport, storage and handling as well as on disposal and ecology can be found in the latest Safety Data Sheet.
-